Tetrazonium salt compound, disazo compound, method for preparing the same, and photosensitive material containing said disazo compound for use in electrophotography

ABSTRACT

The present invention relates to a tetrazonium salt compound having the following general formula (I), ##STR1## wherein X represents an anion functional group. The present invention further relates to a disazo compound having the following general formula (II), ##STR2## wherein A represents ##STR3## (wherein R represents an alkyl such as methyl, ethyl, propyl, butyl or the like, alkoxy, nitro, halogen, cyano or halomethyl group; n represents an integer of 0, 1, 2 or 3; and R may be the same or different when n is an integer of 2 or 3), and a method for preparing the same. The present invention still further relates to a photosensitive material for use in electrophotography, characterized by providing a photosensitive layer containing a disazo pigment having the following general formula (VII), ##STR4## wherein A 1  represents a coupler residue.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a tetrazonium salt compound, disazo compound, a method for preparing the same, and a photosensitive material having a photosensitive layer containing said disazo compound for use in electrophotography.

2. Description of the Prior Art

Heretofore, typically known photosensitive materials include inorganic type photosensitive materials using selenium and its alloy or dispersion of zinc oxide sensitized by coloring matter in binder resin, and organic type photosensitive materials using a charge transfer complex of 2,4,7-trinitro-9-fluorenone (hereinafter referred to as "TNF") and poly-N-vinylcarbazole (hereinafter referred to as "PVK").

However, these conventional photosensitive materials have not only advantages but also various disadvantages. For example, the selenium type photosensitive material widely used at present has such disadvantages as that the manufacturing cost is high due to the severity of the manufacturing conditions; that it is difficult to work the material into a belt-like product because of lack of flexibility; and that it is difficult to handle because the material is weak to heat and mechanical shock. The zinc oxide type photosensitive material can be manufactured at a low expense by coating cheap zinc oxide on a substrate, but has such disadvantages as that the sensitivity is low; that the smoothness of the surface, hardness, tensile strength, friction resistance and other mechanical properties are inferior; and that the durability for repeated use in a plain paper copier is poor. The photosensitive material using the charge transfer complex of TNF and PVK has a low sensitivity and is unsuitable as a photosensitive material for a high speed copier.

Recently, various studies have been carried out to remove disadvantages of these photosensitive materials, and many photosensitive materials, particularly organic type photosensitive materials have been proposed. Among them, a laminated type photosensitive material prepared by forming a thin film of organic pigment on an electro-conductive substrate (charge generating layer) and overlaying a charge transfer material-containing layer (charge transfer layer) on said charge generating layer has generally higher sensitivity and more stable chargeability than the conventional organic type photosensitive materials, and is practically used in part as a photosensitive material for a plain paper copier.

Examples of this kind of known conventional laminated type photosensitive materials include as follows:

(1) photosensitive material using a thin layer formed by vapor depositing perylene derivatives as a charge transfer layer (see U.S. Pat. No. 3,871,882);

(2) photosensitive material using a thin layer formed by coating an organic amine solution of Chloro Dian Blue as a charge generating layer and hydrazone compound as a charge transfer layer (see Japanese Patent Publication No. 55-42380);

(3) photosensitive material using a thin layer formed by coating an organic solvent dispersion of distyryl benzene type disazo compound, stilbene type disazo compound or benzidine type disazo compound as a charge generating layer and hydrazone compound as a charge transfer layer (see Japanese Patent Laid Open Nos. 55-84943, 52-8832 and 52-55643); and the like.

However, these conventional laminated type photosensitive materials have not only advantages but also various disadvantages as mentioned below.

(1) The above photosensitive material using perylene derivatives and oxadiazole derivatives has a disadvantage that the manufacturing cost is very high because of forming a charge generating layer by vapor deposition.

(2) The above photosensitive material using Chloro Dian Blue and hydrazone compound must use an organic amine (for example, ethylene diamine) as a coating solvent for forming a charge generating layer, which is difficult in handling. Furthermore, it has a disadvantage that the image reproducibility of a reddish original is poor because the photosensitive wavelength range of the visible light zone lies in the range of about 450-660 nm. Therefore, it is necessary to provide a filter to cut red light when used in a copier, thus being disadvantageous to the design of a copier.

(3) The above photosensitive materials using distyryl benzene type disazo compound, stilbene type disazo compound or benzidine type disazo compound and hydrazone compound have an advantage that the charge generating layer can easily be prepared simply by coating a dispersion of the disazo compound, but also have a disadvantage that the image reproducibility of a reddish original is poor in the same manner as in the above photosensitive material (2) since the photosensitive wave length lies in the range of about 450-700 nm.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a novel tetrazonium salt to produce a novel disazo compound useful for an electrophotographic element, particularly laminated type electrophotographic element, said novel disazo compound, a method for producing the same, and an electrophotographic element containing said disazo compound. The laminated type electrophotographic element containing said disazo compound of the present invention has a higher sensitivity in comparison with an electrophotographic element containing the conventional disazo compound, and the photosensitive wavelength zone of the electrophotographic element of the present invention resides in a shorter wavelength side of the visible light zone (about 450-600 nm), thus having an excellent image reproducibility of a reddish original.

The novel tetrazonium salt compound of the present invention has the following general formula (I), ##STR5## wherein X represents an anion functional group.

The novel disazo compound of the present invention has the following general formula (II), ##STR6## wherein A represents ##STR7## (wherein R represents an alkyl such as methyl, ethyl, propyl, butyl or the like, alkoxy, nitro, halogen, cyano or halomethyl group; n represents an integer of 0, 1, 2 or 3; and R may be the same or different when n is an integer of 2 or 3).

The method for preparing the novel disazo compound having the above general formula (II) of the present invention is characterized by comprising diazotizing a diamino compound having the formula (III), ##STR8## to prepare a tetrazonium salt having the general formula (I), ##STR9## (wherein X represents an anion functional group), and reacting the tetrazonium salt thus prepared with a compound (hereinafter referred to as a coupler) having the following general formula (IV), (V), (VI) or (VI') ##STR10## (wherein R represents an alkyl, alkoxy, nitro, halogen, cyano or halomethyl group; n represents an integer of 0, 1, 2 or 3; and R may be the same or different when n is an integer of 2 or 3).

The photosensitive material for use in electrophotography of the present invention is characterized by providing a photosensitive layer containing a disazo pigment having the following general formula (VII), ##STR11## wherein A₁ represents a coupler residue.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an infrared absorption spectrum (KBr tablet method) of the tetrazonium salt compound of Preparation Example 1.

FIGS. 2 to 17 show infrared absorption spectrums (KBr tablet method) of typical disazo compounds of the present invention.

FIGS. 18 and 19 are enlarged sectional views showing a structure example of the electrophotographic element of the present invention.

DETAILED DESCRIPTION OF THE PRESENT INVENTION

Tetrazonium salt compound having the formula (I) is a useful intermediate for a disazo compound, and is used in combination with an appropriate coupler to synthesize various types of disazo compounds having a benzophenone structure and having azo group at 3-position and 3'-position. These disazo compounds are expected to be useful photoconductive materials for an electrophotographic element, particularly as a charge generating material.

Typical Examples of an anion functional group of the tetrazonium salt compound of the general formula (I) include ##STR12##

As mentioned above, the disazo compounds having the formulas (II) and (VII) of the present invention are useful as a charge generating material for a laminated type electrophotographic element. These disazo compounds are useful as a charge generating material also for an electrophotographic element having a single layer type photosensitive material having both charge generating material and charge transfer material dispersed in resin, and further useful as a photoconductive material for an electrophotographic element having a photosensitive layer having photoconductive material dispersed in resin.

The photosensitive material containing the disazo compound of the formula (II) or (VII) of the present invention for use in electrophotography can be easily prepared and has a high sensitivity and a photosensitive wave length zone residing in such a shorter wave length zone as to be suitable for reproducing an image of a reddish original.

Examples of the coupler of the disazo compounds expressed by the general formula (VII) include an aromatic hydrocarbon compound and heterocyclic compound having a phenolic hydroxyl group such as phenol type, naphthol type compounds and the like; an aromatic hydrocarbon compound and heterocyclic compound having an amino group; an aromatic hydrocarbon compound and heterocyclic compound having an amino group and a phenolic hydroxyl group such as aminonaphthols; a compound having an aliphatic or aromatic enol type ketone group (compound having an active methylene group) and the like. Preferably, the residue A₁ of the coupler is expressed by the following general formula (VIII), (IX), (X), (XI), (XII), (XIII), (XIV), (XV), (XVI), (XVII) and (XVIII). ##STR13## wherein X₁, Y₁, Z, m and n in the above formula (VIII), (IX), (X) and (XI) represent the following groups: X₁ : --OH, ##STR14## or --NHSO₂ --R₃ (wherein R₁ and R₂ represent hydrogen or a substituted or non-substituted alkyl group, and R₃ represents a substituted or non-substituted alkyl or a substituted or non-substituted aryl group); Y₁ : hydrogen, halogen, substituted or non-substituted alkyl group, substituted or non-substituted alkoxy group, carboxyl group, sulfo group, substituted or non-substituted sulfamoyl group or ##STR15## (wherein R₄ represents hydrogen, alkyl group or its substituted compound, phenyl group or its substituted compound, and Y₂ represents cyclic hydrocarbon or its substituted compound, heterocycle or its substituted compound, or ##STR16## wherein R₅ represents a cyclic hydrocarbon or its substituted compound, heterocycle or its substituted compound, or styryl group or its substituted compound, and R₆ represents hydrogen, alkyl group, phenyl group or their substituted compound, or R₅ and R₆ may form a ring with carbons bonded thereto);

Z: cyclic hydrocarbon or its substituted compound, or heterocycle or its substituted compound;

n: an integer of 1 or 2; and

m: an integer of 1 or 2. ##STR17## wherein R₇ in the above formula (XII) and (XIII) represents a substituted or non-substituted hydrocarbonyl group, and X₁ is the same as mentioned above. ##STR18## wherein R₈ represents an alkyl group, carbamoyl group, carboxyl group or its ester, and Ar₁ represents a cyclic hydrocarbon or its substituted compound, and X₁ is the same as mentioned above. ##STR19## wherein R₉ in the above formula (XV) and (XVI) represents hydrogen or substituted or non-substituted hydrocarbonyl group, and Ar₂ represents cyclic hydrocarbon or its substituted compound.

Examples of the cyclic hydrocarbon expressed by Z in the above general formula (VIII), (IX), (X) or (XI) include benzene ring, naphthalene ring and the like, and examples of the heterocycle expressed by the same include indole ring, carbazole ring, benzofuran ring, ring and the like. Examples of the substituent of the ring expressed by Z include a halogen atom such as chorine, bromine, and the like.

Examples of the cyclic hydrocarbon expressed by Y₂ or R₅ include phenyl, naphthyl, anthryl, pyrenyl and the like, and examples of the heterocyclic group expressed by the same include pyridyl, thienyl, furyl, indolyl, benzofuranyl, carbazolyl, dibenzofuranyl and the like. Examples of the ring formed by bonding R₅ and R₆ include fluorene ring.

Examples of the substituents for the cyclic hydrocarbon or heterocycle expressed by Y₂ or R₅ or for the ring formed by bonding R₅ and R₆ include an alkyl group such as methyl, ethyl, propyl, butyl or the like; an alkoxy group such as methoxy, ethoxy, propoxy, butoxy or the like; a halogen atom such as chlorine, bromine or the like; a dialkyl amino group such as dimethyl amino, diethyl amino or the like; a diaralkyl amino group such as dibenzyl amino or the like; a halomethyl group such trifluoromethyl or the like; nitro group; cyano group; carboxyl group or its ester; hydroxyl group; sulphonate group such as --SO₃ Na; and the like.

Examples of the substituent for the phenyl group expressed by R₄ include a halogen atom such as chlorine or bromine.

Examples of the hydrocarbonyl group expressed by R₇ and R₉ include an alkyl group such as methyl, ethyl, propyl, butyl and the like; an aralkyl group such as benzyl and the like; an aryl group such as phenyl; or their substituted compounds.

Examples of the substituent for the hydrocarbonyl group expressed by R₇ or R₉ include an alkyl group such as methyl, ethyl, propyl, butyl and the like; an alkoxy group such as methoxy, ethoxy, propoxy, butoxy and the like; a halogen atom such as chlorine, bromine and the like; hydroxyl group; nitro group; and the like.

Examples of the cyclic hydrocarbon expressed by Ar₁ or Ar₂ include phenyl, naphthyl and the like, and examples of the substituents for these groups include an alkyl group such as methyl, ethyl, propyl, butyl or the like; an alkoxy group such as methoxy, ethoxy, propoxy, butoxy or the like; nitro group; a halogen group such as chlorine, bromine or the like; cyano group; and a dialkyl amino group such as dimethyl amino, diethyl amino or the like.

Among the groups expressed by X₁, hydroxyl group is particularly suitable.

Among the above coupler residues, preferable ones are expressed by the general formula (IX), (XII), (XIII), (XIV), (XV) and (XVI), and X₁ in the general formula is preferably hydroxyl group. Among them, the coupler residue expressed by the general formula (XVII) ##STR20## (wherein Y₁ and Z are the same as mentioned above) is preferable, and the coupler residue expressed by the general formula (XVIII) ##STR21## (wherein Z, Y₂ and R₂ are the same as mentioned above) is more preferable.

Still more preferable coupler residue among the above mentioned groups is expressed by the general formula (XIX) or (XX) ##STR22## (wherein Z, R₂, R₅ and R₆ are the same as mentioned above, and R₁₀ is the same as those illustrated with regard to the substituents for Y₂).

Examples of the disazo compound of the present invention are illustrated by the following structural formulas.

    __________________________________________________________________________      ##STR23##                                                                     Disazo Compound No.                                                                       R.sub.1                                                                               R.sub.2                                                                            R.sub.3                                                                            R.sub.4                                                                             R.sub.5                                                                            R.sub.6                                                                            R.sub.7                                 __________________________________________________________________________     1          H      H   H   H    H   H   H                                       2          H      NO.sub.2                                                                           H   H    H   H   H                                       3          H      H   NO.sub.2                                                                           H    H   H   H                                       4          H      H   H   NO.sub.2                                                                            H   H   H                                       5          H      CF.sub.3                                                                           H   H    H   H   H                                       6          H      H   CF.sub.3                                                                           H    H   H   H                                       7          H      H   H   CF.sub.3                                                                            H   H   H                                       8          H      CN  H   H    H   H   H                                       9          H      H   CN  H    H   H   H                                       10         H      H   H   CN   H   H   H                                       11         H      I   H   H    H   H   H                                       12         H      H   I   H    H   H   H                                       13         H      H   H   I    H   H   H                                       14         H      Br  H   H    H   H   H                                       15         H      H   Br  H    H   H   H                                       16         H      H   H   Br   H   H   H                                       17         H      Cl  H   H    H   H   H                                       18         H      H   Cl  H    H   H   H                                       19         H      H   H   Cl   H   H   H                                       20         H      F   H   H    H   H   H                                       21         H      H   F   H    H   H   H                                       22         H      H   H   F    H   H   H                                       23         H      CH.sub.3                                                                           H   H    H   H   H                                       24         H      H   CH.sub.3                                                                           H    H   H   H                                       25         H      H   H   CH.sub.3                                                                            H   H   H                                       26         H      C.sub.2 H.sub.5                                                                    H   H    H   H   H                                       27         H      H   H   C.sub.2 H.sub.5                                                                     H   H   H                                       28         H      OCH.sub.3                                                                          H   H    H   H   H                                       29         H      H   OCH.sub.3                                                                          H    H   H   H                                       30         H      H   H   OCH.sub.3                                                                           H   H   H                                       31         H      OC.sub.2 H.sub.5                                                                   H   H    H   H   H                                       32         H      H   OC.sub.2 H.sub.5                                                                   H    H   H   H                                       33         H      H   H   OC.sub.2 H.sub.5                                                                    H   H   H                                       34         H      H   H   N(CH.sub.3).sub.2                                                                   H   H   H                                       35         CH.sub.3                                                                              H   H   H    H   H   H                                       36                                                                                         ##STR24##                                                                            H   H   H    H   H   H                                       37         H      OCH.sub.3                                                                          H   H    OCH.sub.3                                                                          H   H                                       38         H      OC.sub.2 H.sub.5                                                                   H   H    OC.sub.2 H.sub.5                                                                   H   H                                       39         H      CH.sub.3                                                                           H   H    CH.sub.3                                                                           H   H                                       40         H      Cl  H   H    Cl  H   H                                       41         H      CH.sub.3                                                                           H   H    Cl  H   H                                       42         H      OCH.sub.3                                                                          H   OCH.sub.3                                                                           H   H   H                                       43         H      CH.sub.3                                                                           H   CH.sub.3                                                                            H   H   H                                       44         H      CH.sub.3                                                                           H   Cl   H   H   H                                       45         H      NO.sub.2                                                                           H   OCH.sub.3                                                                           H   H   H                                       46         H      H   OCH.sub.3                                                                          H    OCH.sub.3                                                                          H   H                                       47         H      OCH.sub.3                                                                          H   H    Cl  H   H                                       48         H      OCH.sub.3                                                                          H   Cl   OCH.sub.3                                                                          H   H                                       49         H      OCH.sub.3                                                                          H   OCH.sub.3                                                                           Cl  H   H                                       50         H      CH.sub.3                                                                           H   H    H   CH.sub. 3                                                                          H                                       51         H      OCH.sub.3                                                                          H   H    Cl  H   H                                       52         H      CH.sub.3                                                                           H   OCH.sub.3                                                                           H   H   H                                       53         H      OCH.sub.3                                                                          H   Cl   CH.sub.3                                                                           H   H                                       54         H      H   H   H    H   H   OCH.sub.3                               55         H      CH.sub.3                                                                           H   H    H   H   OCH.sub.3                               56         H      OCH.sub.3                                                                          H   Cl   OCH.sub.3                                                                          H   OCH.sub.3                               57         H      OCH.sub.3                                                                          H   H    H   H   Br                                      __________________________________________________________________________

    ______________________________________                                          ##STR25##                                                                     Disazo                                                                         Compound                                                                       No.       A                                                                    ______________________________________                                         58                                                                                        ##STR26##                                                           59                                                                                        ##STR27##                                                           60                                                                                        ##STR28##                                                           61                                                                                        ##STR29##                                                           62                                                                                        ##STR30##                                                           63                                                                                        ##STR31##                                                           64                                                                                        ##STR32##                                                           65                                                                                        ##STR33##                                                           66                                                                                        ##STR34##                                                           67                                                                                        ##STR35##                                                           68                                                                                        ##STR36##                                                           69                                                                                        ##STR37##                                                           70                                                                                        ##STR38##                                                           71                                                                                        ##STR39##                                                           72                                                                                        ##STR40##                                                           73                                                                                        ##STR41##                                                           74                                                                                        ##STR42##                                                           75                                                                                        ##STR43##                                                           76                                                                                        ##STR44##                                                           77                                                                                        ##STR45##                                                           78                                                                                        ##STR46##                                                           79                                                                                        ##STR47##                                                           80                                                                                        ##STR48##                                                           81                                                                                        ##STR49##                                                           82                                                                                        ##STR50##                                                           83                                                                                        ##STR51##                                                           84                                                                                        ##STR52##                                                           85                                                                                        ##STR53##                                                           86                                                                                        ##STR54##                                                           87                                                                                        ##STR55##                                                           88                                                                                        ##STR56##                                                           89                                                                                        ##STR57##                                                           90                                                                                        ##STR58##                                                           91                                                                                        ##STR59##                                                           92                                                                                        ##STR60##                                                           93                                                                                        ##STR61##                                                           94                                                                                        ##STR62##                                                           95                                                                                        ##STR63##                                                           96                                                                                        ##STR64##                                                           97                                                                                        ##STR65##                                                           98                                                                                        ##STR66##                                                           99                                                                                        ##STR67##                                                           100                                                                                       ##STR68##                                                           101                                                                                       ##STR69##                                                           102                                                                                       ##STR70##                                                           103                                                                                       ##STR71##                                                           104                                                                                       ##STR72##                                                           105                                                                                       ##STR73##                                                           106                                                                                       ##STR74##                                                           107                                                                                       ##STR75##                                                           108                                                                                       ##STR76##                                                           109                                                                                       ##STR77##                                                           110                                                                                       ##STR78##                                                           111                                                                                       ##STR79##                                                           112                                                                                       ##STR80##                                                           113                                                                                       ##STR81##                                                           114                                                                                       ##STR82##                                                           115                                                                                       ##STR83##                                                           116                                                                                       ##STR84##                                                           117                                                                                       ##STR85##                                                           118                                                                                       ##STR86##                                                           119                                                                                       ##STR87##                                                           120                                                                                       ##STR88##                                                           ______________________________________                                    

    ______________________________________                                          ##STR89##                                                                      ##STR90##                                                                     Disazo Com-                                                                    pound No.                                                                               R.sub.22 R.sub.33                                                                               R.sub.44                                                                               R.sub.55                                                                             R.sub.66                               ______________________________________                                         121      H        H       H       H     H                                      122      NO.sub.2 H       H       H     H                                      123      H        NO.sub.2                                                                               H       H     H                                      124      H        H       NO.sub.2                                                                               H     H                                      125      Cl       H       H       H     H                                      126      H        Cl      H       H     H                                      127      H        H       Cl      H     H                                      128      CH.sub.3 H       H       H     H                                      129      H        CH.sub.3                                                                               H       H     H                                      130      H        H       CH.sub.3                                                                               H     H                                      131      C.sub.2 H.sub.5                                                                         H       H       H     H                                      132      H        H       C.sub.2 H.sub.5                                                                        H     H                                      133      OCH.sub.3                                                                               H       H       H     H                                      134      H        OCH.sub.3                                                                              H       H     H                                      135      H        H       OCH.sub.3                                                                              H     H                                      136      OC.sub.2 H.sub.5                                                                        H       H       H     H                                      137      H        H       OC.sub.2 H.sub.5                                                                       H     H                                      138      CH.sub.3 H       OCH.sub.3                                                                              H     H                                      139      CH.sub.3 H       CH.sub.3                                                                               H     H                                      140      CH.sub.3 H       H       CH.sub.3                                                                             H                                      141      CH.sub.3 H       H       H     CH.sub.3                               142      OCH.sub.3                                                                               H       OCH.sub.3                                                                              H     H                                      143      OCH.sub.3                                                                               H       H       OCH.sub.3                                                                            H                                      144      H        OCH.sub.3                                                                              H       OCH.sub.3                                                                            H                                      145      CH.sub.3 Cl      H       H     H                                      146      CH.sub.3 H       Cl      H     H                                      147      CH.sub.3 H       H       Cl    H                                      ______________________________________                                    

    ______________________________________                                          ##STR91##                                                                      ##STR92##                                                                     Disazo com-                                                                    pound No. R.sub.222                                                                               R.sub.333                                                                               R.sub.444                                                                             R.sub.555                                                                            R.sub.666                             ______________________________________                                         148       H        H        H      H     H                                     149       NO.sub.2 H        H      H     H                                     150       H        NO.sub.2 H      H     H                                     151       H        H        NO.sub.2                                                                              H     H                                     152       Cl       H        H      H     H                                     153       H        Cl       H      H     H                                     154       H        H        Cl     H     H                                     155       CH.sub.3 H        H      H     H                                     156       H        CH.sub.3 H      H     H                                     157       H        H        CH.sub.3                                                                              H     H                                     158       OCH.sub.3                                                                               H        H      H     H                                     159       H        OCH.sub.3                                                                               H      H     H                                     160       H        H        OCH.sub.3                                                                             H     H                                     161       CH.sub.3 H        OCH.sub.3                                                                             H     H                                     162       OCH.sub.3                                                                               H        Cl     CH.sub.3                                                                             H                                     163       CH.sub.3 H        H      H     CH.sub.3                              ______________________________________                                    

    __________________________________________________________________________      ##STR93##                                                                     Disazo                                                                         Compound                                                                       No.   R.sub.10  R.sub.20                                                                           R.sub.30                                                                            R.sub.40                                                                            R.sub.50    R.sub.60                             __________________________________________________________________________     164   II        H   H    H    H           H                                    165   H         NO.sub.2                                                                           H    H    H           H                                    166   H         H   NO.sub.2                                                                            H    H           H                                    167   H         H   H    NO.sub.2                                                                            H           H                                    168   H         Cl  H    H    H           H                                    169   H         H   Cl   H    H           H                                    170   H         H   H    Cl   H           H                                    171   H         CH.sub.3                                                                           H    H    H           H                                    172   H         H   CH.sub.3                                                                            H    H           H                                    173   H         H   H    CH.sub.3                                                                            H           H                                    174   H         OCH.sub.3                                                                          H    H    H           H                                    175   H         H   OCH.sub.3                                                                           H    H           H                                    176   H         H   H    OCH.sub.3                                                                           H           H                                    177   H         H   H    N(CH.sub.3).sub.2                                                                   H           H                                    178   H         F   H    H    H           H                                    179   H         H   F    H    H           H                                    180   H         H   H    F    H           H                                    181   H         Br  H    H    H           H                                    182   H         H   Br   H    H           H                                    183   H         H   H    Br   H           H                                    184   H         Cl  H    Cl   H           H                                    185   H         H   Cl   Cl   H           H                                    186   H         CN  H    H    H           H                                    187   H         H   H    CN   H           H                                    188   H         CH.sub.3                                                                           H    CH.sub.3                                                                            H           H                                    189   H         OCH.sub.3                                                                          H    H    OCH.sub.3   H                                    190   H         OCH.sub.3                                                                          OCH.sub.3                                                                           OCH.sub.3                                                                           H           H                                    191   H         CH.sub.3                                                                           H    H    H           CH.sub.3                             192   CH.sub.3  H   H    H    H           H                                    193                                                                                   ##STR94##                                                                               H   H    H    H           H                                    194                                                                                   ##STR95##                                                                               H   H    H    H           H                                    195   H         H   H    H                                                                                    ##STR96##  H                                    __________________________________________________________________________

    ______________________________________                                          ##STR97##                                                                

    ______________________________________                                          ##STR98##                                                                     Disazo                                                                         Compound No.                                                                               R.sub.8                                                                               R.sub.9                                                     ______________________________________                                         196         CH.sub.3                                                                              CH.sub.3                                                    197         H                                                                                      ##STR99##                                                  198         H                                                                                      ##STR100##                                                 199         H                                                                                      ##STR101##                                                 200         H                                                                                      ##STR102##                                                 201         H                                                                                      ##STR103##                                                 202         CH.sub.3                                                                               ##STR104##                                                 203         H                                                                                      ##STR105##                                                 204         H                                                                                      ##STR106##                                                 205         H                                                                                      ##STR107##                                                 206         H                                                                                      ##STR108##                                                 207         H                                                                                      ##STR109##                                                 ______________________________________                                          ##STR110##                                                                    Disazo                                                                         Compound No.    X.sub.1                                                        ______________________________________                                         206                                                                                             ##STR111##                                                    209                                                                                             ##STR112##                                                    210                                                                                             ##STR113##                                                    ______________________________________                                    

    __________________________________________________________________________      ##STR114##                                                                     ##STR115##                                                                    Disazo                                                                         Compound                                                                       No.   R.sub.100 R.sub.200                                                                          R.sub.300                                                                          R.sub.400                                                                           R.sub.500   R.sub.600                             __________________________________________________________________________     211   H         H   H   H    H           H                                     212   H         NO.sub.2                                                                           H   H    H           H                                     213   H         H   NO.sub.2                                                                           H    H           H                                     214   H         H   H   NO.sub.2                                                                            H           H                                     215   H         Cl  H   H    H           H                                     216   H         H   Cl  H    H           H                                     217   H         H   H   Cl   H           H                                     218   H         CH.sub.3                                                                           H   H    H           H                                     219   H         H   CH.sub.3                                                                           H    H           H                                     220   H         H   H   CH.sub.3                                                                            H           H                                     221   H         OCH.sub.3                                                                          H   H    H           H                                     222   H         H   OCH.sub.3                                                                          H    H           H                                     223   H         H   H   OCH.sub.3                                                                           H           H                                     224   H         H   H   N(CH.sub.3).sub.2                                                                   H           H                                     225   H         F   H   H    H           H                                     226   H         H   F   H    H           H                                     227   H         H   H   F    H           H                                     228   H         Br  H   H    H           H                                     229   H         H   Br  H    H           H                                     230   H         H   H   Br   H           H                                     231   H         Cl  H   Cl   H           H                                     232   H         H   Cl  Cl   H           H                                     233   H         CN  H   H    H           H                                     234   H         H   H   CN   H           H                                     235   H         CH.sub.3                                                                           H   CH.sub.3                                                                            H           H                                     236   H         OCH.sub.3                                                                          H   H    OCH.sub.3   H                                     237   H         OCH.sub.3                                                                          OCH.sub.3                                                                          OCH.sub.3                                                                           H           H                                     238   H         CH.sub.3                                                                           H   H    H           CH.sub.3                              239   CH.sub.3  H   H   H    H           H                                     240                                                                                   ##STR116##                                                                              H   H   H    H           H                                     241                                                                                   ##STR117##                                                                              H   H   H    H           H                                     242   H         H   H   H                                                                                    ##STR118## H                                     __________________________________________________________________________

    ______________________________________                                          ##STR119##                                                               

    ______________________________________                                          ##STR120##                                                                    Disazo                                                                         Compound                                                                       No.       R.sub.80 R.sub.90                                                    ______________________________________                                         243       CH.sub.3 CH.sub.3                                                    244       H                                                                                        ##STR121##                                                 245       H                                                                                        ##STR122##                                                 246       H                                                                                        ##STR123##                                                 247       H                                                                                        ##STR124##                                                 248       H                                                                                        ##STR125##                                                 249       CH.sub.3                                                                                 ##STR126##                                                 250       H                                                                                        ##STR127##                                                 251       H                                                                                        ##STR128##                                                 252       H                                                                                        ##STR129##                                                 253       H                                                                                        ##STR130##                                                 254       H                                                                                        ##STR131##                                                 ______________________________________                                          ##STR132##                                                                    Disazo                                                                         Compound                                                                       No.                 X.sub.2                                                    ______________________________________                                         255                                                                                                 ##STR133##                                                256                                                                                                 ##STR134##                                                257                                                                                                 ##STR135##                                                ______________________________________                                    

A tetrazonium salt having the general formula (I) of the present invention can be obtained by reducing, for example, 4,4'-dichloro-3,3'-dinitrobenzophenone to prepare 4,4'-dichloro-3,3'-diaminobenzophenone, and diazotizing the diamino compound thus prepared.

The diazotization of 4,4'-dichloro-3,3'-diaminobenzophenone is carried out in an inorganic acid such as hydrochloric acid or sulfuric acid by adding sodium nitrite at -10° C. to 20° C. This diazotization is completed in 30 minutes to 3 hours. To the reaction mixture, is added borofluoric acid, sodium borofluoride aqueous solution or the like to obtain a tetrazonium salt.

A disazo compound having the general formula (II) has been prepared (a) by reacting the above diazotization reaction solution directly with a coupler or (b) by adding borofluoric acid, sodium borofluoride aqueous solution or the like to the above diazotization reaction solution to precipitate as a tetrazonium salt, isolating the precipitated tetrazonium salt and reacting the isolated tetrazonium salt with a coupler. From the stoichiometrical view point, one mole of a tetrazonium salt is reacted with two moles of a coupler, but from practical view point, 1.5-4 moles, preferably 2-3 moles of the coupler is supplied to one mole of the tetrazonium salt when taking manufacturing cost and the purity of pigment obtained into consideration. In practice, this reaction is carried out by dissolving a mixture of the tetrazonium salt and coupler in an organic solvent such as N,N-dimethylformaldehyde (DMF), dimethylsulfoxide or the like, and adding drop-wise an alkaline aqueous solution to the reaction solution such as sodium acetate aqueous solution at about -10° C. to 40° C. This reaction is completed in about 5 minutes to 3 hours. After the completion of the reaction, the precipitated crystal is filtered out and is finally purified by an appropriate method (for example by washing, recrystalizing or the like with water and/or organic solvent). The novel disazo compound prepared in accordance with the present invention as mentioned above, is a colored crystal at normal temperature.

The following Examples illustrate the preparation of a tetrazonium salt and a disazo compound of the present invention.

PREPARATION EXAMPLE 1 (Preparation of Tetrazonium Salt)

3,3'-diamino-4,4'-dichlorobenzophenone 28.1 g was added to a hydrochloric acid aqueous solution comprising water 200 ml and conc. hydrochloric acid 52 ml, and the resultant mixture was heated at about 60° C. for one hour, thereafter being cooled to 0° C. To the cooled mixture, was added drop-wise at a temperature of 0° C. to 5° C. for 20 minutes a solution prepared by dissolving sodium nitrite 14.9 g in water 50 ml. The resultant mixture was stirred at the same temperature for 30 minutes. 42% borofluoric acid 90 ml was added to the resultant reaction solution to precipitate a crystal. The precipitated crystal was filtered out, and the crystal was subjected to washing with water and drying, thus obtaining a light brown crystal of tetrazonium difluoroborate 37.7 g (yield=78.7%). An infrared absorption spectrum (KBr tablet method) of this product is shown in FIG. 1. An absorption band on the basis of N₂ ⁺ appeared at 2280 cm⁻¹ and an absorption band on the basis of >C═O appeared at 1700 cm⁻¹.

PREPARATION EXAMPLE 2 (Preparation of Disazo Compund No. 1)

1.20 g of the tetrazonium salt prepared in the above Example 1 and 1.32 g (two times mol of tetrazonium salt) of 2-hydroxy-3-naphthoic acid anilide as a coupler were dissolved in 150 ml of cooled N,N-dimethylformamide. To this solution, was added drop-wise a solution comprising sodium acetate 0.82 g and water 7 ml at a temperature of 5°-10° C. for 20 minutes. Thereafter, the resultant mixture was stirred for 3 hours at room temperature. The produced precipitate was filtered out, and was washed for 3 times with N,N-dimethylformamide 200 ml heated to 80° C. and further with water 700 ml for 2 times. The washed precipitate was dried at 80° C. under a reduced pressure of 2 mm Hg, thus obtaining 1.55 g (yield=74.9%) of the above disazo compound No. 1 shown in Table 1.

The appearance of disazo compound thus obtained was reddish orange color powder, the infrared absorption spectrum (KBr tablet method) of which is shown in FIG. 2.

PREPARATION EXAMPLES 3 TO 17

The same procedure as in the above Preparation Example 2 was repeated, except that compounds as mentioned in the following Table 3 were used as couplers to prepare the disazo compounds shown in Tables 1 and 2. The yields and appearances of the disazocompounds thus obtained are shown in Table 3.

                                      TABLE 1                                      __________________________________________________________________________      ##STR136##                                                                                                          Infrared                                 Disazo            Elemental Analysis                                                                         Decomposition                                                                          Absorption                               Compound          (Calculated Value)                                                                         Point   Spectrum                                 No.   R.sub.1                                                                            R.sub.2                                                                            R.sub.3                                                                            C % H % N % (°C.)                                                                           (KBr Disk)                               __________________________________________________________________________      1    H   H   H   67.50                                                                              3.38                                                                               10.01                                                                              324     FIG. 2                                                     (68.04)                                                                            (3.64)                                                                             (10.13)                                              28    OCH.sub.3                                                                          H   H   66.14                                                                              3.97                                                                               9.44                                                                               328     FIG. 3                                                     (66.14)                                                                            (3.85)                                                                             (9.45)                                               29    H   OCH.sub.3                                                                          H   66.13                                                                              3.77                                                                               9.34                                                                               314     FIG. 4                                                     (66.14)                                                                            (3.85)                                                                             (9.45)                                               30    H   H   OCH.sub.3                                                                          65.95                                                                              3.57                                                                               9.37                                                                               332     FIG. 5                                                     (66.14)                                                                            (3.85)                                                                             (9.45)                                               23    CH.sub.3                                                                           H   H   68.60                                                                              3.98                                                                               9.64                                                                               330     FIG. 6                                                     (68.61)                                                                            (3.99)                                                                             (9.80)                                               24    H   CH.sub.3                                                                           H   68.79                                                                              3.81                                                                               9.77                                                                               310     FIG. 7                                                     (68.61)                                                                            (3.99)                                                                             (9.80)                                               25    H   H   CH.sub.3                                                                           68.61                                                                              3.79                                                                               9.74                                                                               332     FIG. 8                                                     (68.61)                                                                            (3.99)                                                                             (9.80)                                               17    Cl  H   H   62.96                                                                              2.96                                                                               9.31                                                                               348     FIG. 9                                                     (62.82)                                                                            (3.14)                                                                             (9.36)                                               18    H   Cl  H   62.94                                                                              2.95                                                                               9.27                                                                               350      FIG. 10                                                   (62.82)                                                                            (3.14)                                                                             (9.36)                                               19    H   H   Cl  62.82                                                                              2.95                                                                               9.22                                                                               328      FIG. 11                                                   (62.82)                                                                            (3.14)                                                                             (9.36)                                                2    NO.sub.2                                                                           H   H   61.47                                                                              2.82                                                                               12.09                                                                              364      FIG. 12                                                   (61.38)                                                                            (3.09)                                                                             (12.16)                                               3    H   NO.sub.2                                                                           H   61.13                                                                              3.15                                                                               12.01                                                                              340      FIG. 13                                                   (61.38)                                                                            (3.09)                                                                             (12.16)                                               4    H   H   NO.sub.2                                                                           61.14                                                                              2.86                                                                               11.95                                                                              360      FIG. 14                                                   (61.38)                                                                            (3.09)                                                                             (12.16)                                              __________________________________________________________________________

                                      TABLE 2                                      __________________________________________________________________________      ##STR137##                                                                                                                   Infrared                        Disazo                     Elemental Analysis                                                                         Decomposition                                                                          Absorption                      Compound                   (Calculated Value)                                                                         Point   Spectrum                        No.   Ar                   C % H % N % (°C.)                                                                           (KBr Disk)                      __________________________________________________________________________     121                                                                                   ##STR138##          69.82 (70.30)                                                                      3.67 (3.60)                                                                        10.71 (11.12)                                                                      322     FIG. 15                         164                                                                                   ##STR139##          66.60 (66.59)                                                                      3.53 (3.65)                                                                        12.47 (12.68)                                                                      318     FIG. 16                          71                                                                                   ##STR140##          61.60 (61.89)                                                                      2.69 (2.93)                                                                        11.01 (11.11)                                                                      348     FIG. 17                         __________________________________________________________________________

                                      TABLE 3                                      __________________________________________________________________________     Disazo                                                                         Compound                                                                       No.   Coupling Component    Yield (%)                                                                            Appearance                                   __________________________________________________________________________     28                                                                                    ##STR141##           66.7  reddish orange                               29                                                                                    ##STR142##           72.5  reddish orange                               30                                                                                    ##STR143##           74.3  reddish orange                               23                                                                                    ##STR144##           80.4  reddish orange                               24                                                                                    ##STR145##           69.2  red                                          25                                                                                    ##STR146##           76.2  reddish orange                               17                                                                                    ##STR147##           82.2  reddish orange                               18                                                                                    ##STR148##           71.1  reddish orange                               19                                                                                    ##STR149##           81.3  reddish orange                                2                                                                                    ##STR150##           89.1  reddish orange                                3                                                                                    ##STR151##           83.5  red                                           4                                                                                    ##STR152##           87.0  reddish orange                               121                                                                                   ##STR153##           38.5  bluish purple                                164                                                                                   ##STR154##           90.5  reddish orange                               71                                                                                    ##STR155##           54.5  reddish orange                               __________________________________________________________________________

The disazo pigment of the present invention is used as a charge generating material in a photosensitive layer of an electrophotographic element. FIGS. 18 and 19 illustrate a typical structure of the electrophotographic element.

The electrophotographic element of FIG. 18 comprises a laminated type photosensitive layer 191 on an electroconductive substrate 11, said photosensitive layer 191 comprising a charge generating layer 15 containing disazo pigment 13 as the main component and a charge transfer layer 17 containing charge transfer material as the main component.

In the electrophotographic element of FIG. 18, exposed light passes through a charge transfer layer to a charge generating layer 15 wherein charge is generated in disazo pigment 13. The charge thus generated is transferred by the charge transfer layer 17. Thus, the generation of charge necessary for light decay is effected in disazo pigment 13, and the transfer of the generated charge is effected by the charge transfer layer 17.

The electrophotographic element shown in FIG. 19 is composed of a photosensitive layer 192 on an electroconductive substrate 11, the photosensitive layer 192 comprising essentially of disazo pigment 13, charge transfer material and insulative binder. The disazo pigment 13 is a charge generating material.

It is possible to modify the basic structure of the electrophotographic element of FIG. 18, for example, by applying the charge generating layer and the charge transfer layer in reverse order.

The thickness of the charge generating layer 15 of the photosensitive layer of FIG. 18 is preferably 0.01-5μ, more preferably 0.05-2μ. If this thickness is less than 0.01μ, the generation of charge is not satisfactory. On the other hand, if this thickness is more than 5μ, the residual potential becomes too high for practical use.

The thickness of the charge transfer layer 17 is preferably 3-50μ, more preferably 5-20μ. If this thickness is less than 3μ, a charged amount is insufficient. On the other hand, if this thickness is more than 50μ, the residual potential becomes too high for practical use.

The charge generating layer 15 contains disazo pigment expressed by the above general formula as the main component, and further binder, plasticizer and the like. The amount of disazo pigment in the charge generating layer is more than 30% by weight, more preferably 50% by weight.

The charge transfer layer 17 contains charge transfer material and binder as the main components and further plasticizer and the like. The amount of the charge transfer material in the charge transfer layer is 10-95% by weight, preferably 30-90% by weight. If the amount of the charge transfer material is less than 10% by weight, the transfer of the charge is not substantially carried out. On the other hand, if this amount is more than 95% by weight, the mechanical strength of the photosensitive film is too poor for practical use.

The photosensitive layer 192 of the photosensitive element of FIG. 19 is preferably 3-50μ, more preferably 5-20μ. The amount of the disazo pigment in the photosensitive layer 192 is preferably less than 50% by weight, more preferably less than 20% by weight, and the amount of the charge transfer material is preferably 10-95% by weight, more preferably 30-90% by weight.

The essential feature of the present invention resides in the use of specific disazo pigments as expressed by the above general formula (II) and (VII), and other components such as electroconductive substrate, charge transfer material and the like are the same as the conventionally known materials. Examples of these materials are illustrated hereinafter.

Examples of the electroconductive substrate used in the electrophotgraphic element of the present invention include: metallic plates such as aluminum, copper, zinc and the like; plastic sheets such as polyester and the like; plastic film composite obtained by vapor depositing electroconductive materials such as aluminum, SnO₂ and the like on a plastic film; or electroconductively treated paper and the like.

Examples of binders include: condensation type resins such as polyamide, polyurethane, polyester, epoxy resin, polyketone, polycarbonate and the like; vinyl polymers such as polyvinyl ketone, polystyrene, poly-N-vinyl carbazole, polyacrylamide, and the like. Any resin can be used if it is insulative and adhesive.

Examples of plasticizers include halogenated paraffin, polybiphenylchloride, dimethylnaphthalene, dibutyl phthalate and the like. Silicone oil may also be added to improve surface properties of the photosensitive material.

The charge transfer material includes a positive hole transfer material and an electron transfer material. Examples of the hole transfer material include compounds as expressed by the following general formulas (a) to (k). ##STR156## (wherein R₁₁₅ represents methyl, ethyl, 2-hydroxyethyl or 2-chloroethyl; R₁₂₅ represents methyl, ethyl, benzyl or phenyl; and R₁₃₅ represents hydrogen, chlorine, bromine, alkyl having 1 to 4 carbon atoms, alkoxy having 1 to 4 carbon atoms, dialkylamino or nitro.) ##STR157## (wherein Ar₃ represents naphthalene ring, anthracene ring, styryl and their substituents or pyridine ring furan ring, or thiophene ring; and R₁₄₅ represents alkyl or benzyl.) ##STR158## (wherein R₁₅₅ represents alkyl, benzyl, phenyl or naphthyl; R₁₆₅ represents hydrogen, alkyl having 1 to 3 carbon atoms, alkoxy having 1 to 3 carbon atoms, dialkylamino, diaralkylamino or diarylamino; n represents an integer of 1 to 4; when n is 2 or more, R₁₆₅ may be the same or different; and R₁₇₅ represents hydrogen or methoxy.) ##STR159## (wherein R₁₈₅ represents alkyl having 1 to 11 carbon atoms, substituted or non-substituted phenyl or heterocyclic group; R₁₉₅ and R₂₀₅ may be the same or different and represent hydrogen, alkyl having 1 to 4 carbon atoms, hydroxyalkyl, chloroalkyl, substituted or non-substituted aralkyl; R₁₉₅ and R₂₀₅ may be bonded with each other to form a heterocyclic ring containing nitrogen; R₂₁₅ may be the same or different and represents hydrogen, alkyl having 1 to 4 carbon atoms, alkoxy or halogen.) ##STR160## (wherein R₂₂₅ represents hydrogen or a halogen atom; and Ar₄ represents a substituted or non-substituted phenyl, naphthyl, anthryl or carbazolyl.) ##STR161## (wherein R₂₃₅ represents hydrogen, halogen, cyano, alkoxy having 1 to 4 carbon atoms or alkyl having 1 to 4 carbon atoms; Ar₅ represents ##STR162## wherein R₂₄₅ represents alkyl having 1 to 4 carbon atoms, R₂₅₅ represents hydrogen, halogen, alkyl having 1 to 4 carbon atoms, alkoxy having 1 to 4 carbon atoms or dialkyl amino, n is an integer of 1 or 2; when n is 2, R₂₅₅ may be the same or different; R₂₆₅ and R₂₇₅ represent hydrogen, substituted or non-substituted alkyl having 1 to 4 carbon atoms or substituted or non-substituted benzyl group.) ##STR163## (wherein R₂₈₅ and R₂₉₅ represents carbazolyl, pyridyl, thienyl, indolyl, furyl, or substituted or non-substituted phenyl, styryl, naphthyl or anthryl group; these substituents are selected from the group of dialkylamino, alkyl, alkoxy, carboxyl or its ester, halogen atom, cyano, aralkylamino, N-alkyl-N-aralkylamino, amino, nitro and acetyl amino groups.) ##STR164## (wherein R₃₀₅ represents a lower alkyl or benzyl group; R₃₁₅ represents hydrogen, lower alkyl, lower alkoxy, halogen, nitro, amino, or amino group substituted with lower alkyl or benzyl; and n is an integer of 1 or 2.) ##STR165## (wherein R₃₂₅ represents hydrogen, alkyl, alkoxy or halogen; R₃₃₅ and R₃₄₅ represent alkyl, substituted or non-substituted aralkyl, or substituted or non-substituted aryl group; R₃₅₅ represents hydrogen or substituted or non-substituted phenyl; and Ar₆ represents phenyl or naphthyl group.) ##STR166## (wherein n is an integer of 0 or 1; R₃₆₅ represents hydrogen, alkyl or substituted or non-substituted phenyl; A₁ represents ##STR167## 9-anthryl, or substituted or non-substituted N-alkylcarbazolyl group, wherein R₃₇₅ represents hydrogen, alkyl, alkoxy, halogen or ##STR168## wherein R₃₈₅ and R₃₉₅ represent alkyl, substituted or non-substituted aralkyl, or substituted or non-substituted aryl group, and R₃₈₅ and R₃₉₅ may form a ring; and m is an integer of 0, 1, 2 or 3, when m is 2 or more, R₃₇₅ may be the same or different.) ##STR169## (wherein R₄₀₅, R₄₁₅ and R₄₂₅ are hydrogen, lower alkyl, lower alkoxy, dialkylamino, or halogen; and n is 0 or 1.)

Examples of the compound expressed by the general formula (a) include: 9-ethylcarbazole-3-aldehyde-1-methyl-1-phenylhydrazone, 9-ethylcarbazole-3-aldehyde-1-benzyl-1-phenylhydrazone, 9-ethylcarbazole-3-aldehyde 1,1-diphenylhydrazone, and the like.

Examples of the compound expressed by the general formula (b) include: 4-diethylaminostyrene-β-aldehyde-1-methyl-1-phenylhydrazone, 4-methoxynaphthalene-1-aldehyde-1-benzyl-1-phenylhydrazone, and the like.

Examples of the compound expressed by the general formula (c) include: 4-methoxybenzaldehyde 1-methyl-1-phenylhydrazone, 2,4-dimethoxybenzaldehyde 1-benzyl-1phenylhydrazone, 4-diethylaminobenzaldehyde 1,1-diphenylhydrazone, 4-methoxybenzaldehyde 1-benzyl-1-(4-methoxy)phenyl hydrazone, 4-diphenylaminobenzaldehyde-1-benzyl-1-phenylhydrazone, 4-dibenzylaminobenzaldehyde 1,1-diphenylhydrazone and the like.

Examples of the compound expressed by the general formula (d) include: 1,1-bis(4-dibenzylaminophenyl)propane, tris(4-diethylaminophenyl)methane, 1,1-bis(4-dibenzylaminophenyl)propane, 2,2'-dimethyl-4,4'-bis(diethylamino)-triphenylmethane and the like.

Examples of the compound expressed by the general formula (e) include: 9-(4-diethylaminostyryl)anthracene, 9-bromo-10-(4-diethylaminostyryl)anthracene, and the like.

Examples of the compound expressed by the general formula (f) include: 9-(4-dimethylaminobenzylidene)fluorene, 3-(9-fluorenylidene)-9-ethylcarbazole, and the like.

Examples of the compound expressed by the general formula (g) include: 1,2-bis(4-diethylaminostyryl)benzene, 1,2-bis(2,4-dimethoxystyryl)benzene and the like.

Examples of the compound expressed by the general formula (h) include: 3-styryl-9-ethylcarbazole, 3-(4-methoxystyryl)-9-ethylcarbazole, and the like.

Examples of the compound expressed by the general formula (i) include: 4-diphenylaminostilbene, 4-dibenzylaminostilbene, 4-ditolylaminostilbene, 1-(4-diphenylaminostyryl)naphthalene, 1-(4-diethylaminostyryl)naphthalene, and the like.

Examples of the compound expressed by the general formula (j) include: 4'-diphenylaminoalpha-phenylstilbene, 4'-methylphenylamino-alpha-phenylstilbene, and the like.

Examples of the compound expressed by the general formula (k) include: 1-phenyl-3-(4-diethylaminostyryl)-5-(4-diethylaminophenyl)pyrazoline, 1-phenyl-3-(4-dimethylaminostyryl)-5-(4-dimethylaminophenyl)pyrazoline, and the like.

Other examples of positive hole transfer material include: oxadiazole compounds such as 2,5-bis(4-diethylaminophenyl)-1,3,4-oxadiazole, 2,5-bis(4-(4-diethylaminostyryl)phenyl)-1,3,4-oxadiazole, 2-(9-ethylcarbazolyl-3)-5-(4-diethylaminophenyl)-1,3,4-oxadiazole, and the like; low molecular oxazole compounds such as 2-vinyl-4-(2-chlorophenyl)-5-(4-diethylaminophenyl)-oxazole, 2-(4-diethylaminophenyl)-4-phenyloxazole, and the like; and high molecular compounds such as poly-N-vinyl carbazole, halogenated poly-N-vinyl carbazole, polyvinyl pyrene, polyvinyl anthracene, pyrene formaldehyde resin, ethylcarbazole formaldehyde resin, and the like.

Examples of electron transfer material include: chloroanil, bromoanil, tetracyanoethylene, tetracyanoquinonedimethane, 2,4,7-trinitro-9-fluorenone, 2,4,5,7-tetranitro-9-fluorenone, 2,4,5,7-tetranitroxanthone, 2,4,8-trinitro-thioxanthone, 2,6,8-trinitro-4H-indeno(1,2-b)-thiophene-4on, 1,3,7-trinitrodibenzothiophene-5,5-dioxide, and the like.

These charge transfer materials are used alone or in the form of a mixture of two or more.

With regard to the electrophotographic elements as prepared above, an adhesive layer or barrier layer may optionally be applied between an electroconductive substrate and a photosensitive layer. Examples of these layers include polyamide, nitrocellulose, aluminum oxide and teh like. The thickness of the layer is preferably not more that 1μ.

The electrophotographic element as shown in FIG. 18 is prepared by vapor-depositing disazo pigment on an electroconductive substrate in accordance with vacuum vapor depositing method as disclosed in U.S. Pat. Nos. 3,973,959 and 3,996,049 or coating and drying on an electroconductive substrate a dispersion of disazo pigment particles in an appropriate solvent optionally having a binder dissolved; and then coating and drying a solution containing charge transfer material and binder on the charge generating layer, the surface of which may optionally be subjected to a buff polishing as disclosed in Japanese Patent Laid Open No. 51-90827, or the thickness of which may be regulated.

The electrophotographic element as shown in FIG. 19 is prepared by dispersing disazo pigment particles in a solution having charge transfer material and binder dissolved, coating the dispersion on an electroconductive substrate and drying. In any case, disazo pigment used in the present invention is powdered by a ball mill or the like to a particle size of not more than 5μ, preferably not more than 2μ. Coating can be effected by ordinary method by means of doctor blade, dipping, wire bar and the like.

Copying by the electrophotographic element of the present invention can be effected by developing after charging and explosing the photosensitive layer surface and, if necessary, transferring the developed image to paper and the like.

As clearly seen from the above description and the following Examples, the electrophotographic element of the present invention using disazo pigment having the benzophenone structure as a charge generating material can be more easily produced in comparison with the conventional electrophotographic elements. In addition to this advantage, the performances of the electrophotographic element of the present invention are stable even if it is repeatedly used a great number of times.

The present invention is further illustrated by the following Examples, but the present invention the should not be limited thereto.

EXAMPLE 1

76 parts by weight of disazo pigment No. 18, 1260 parts by weight of tetrahydrofuran solution (solid content=2%) of polyester resin ("Byron 200" manufactured by Toyo Boseki Ltd.), and 3700 parts by weight of tetrahydrofuran are powdered and mixed in a ball mill. The dispersion thus obtained was coated on an aluminum surface of an aluminum-deposited polyester base (electroconductive substrate) by a doctor blade, and the coated film was allowed to stand for drying, thereby forming a charge generating layer having a thickness of about 1 μm.

On this charge generating layer, was coated a solution prepared by dissolving and mixing 2 parts by weight of 9-ethylcarbazole-3-aldehyde 1-methyl-1-phenylhydrazone, 2 parts by weight of polycarbonate resin ("Panlight K-1300" manufactured by Teijin Co., Ltd.) and 16 parts by weight of tetrahydrofuran by a doctor blade, and the coated film was dried at 80° C. for 2 minutes and 105° C. for 5 minutes, thereby forming a charge transfer layer having a thickness of about 20 μm. The laminated type electrophotographic element No. 1 thus prepared is shown in FIG. 18.

EXAMPLE 2 TO 8

Electrophotographic elements Nos. 2 to 8 were prepared in the same manner as in Example 1, except that disazo pigments as shown in the following Table 4 were used in place of disazo pigment No. 18 used in Example 1.

EXAMPLES 9 TO 12

Electrophotographic elements Nos. 9 to 12 were prepared in the same manner as in Example 1, except that 1-phenyl-3-(4-diethylaminostyryl)-5-(4-diethylaminophenyl)pyrazoline was used as a charge transfer material and disazo pigments as shown in the following Table 5 were used.

EXAMPLES 13 TO 20

Electrophotographic elements Nos. 13 to 20 were prepared in the same manner as in Example 1, except that 4'-diphenylamino-alpha-phenylstilbene was used as a charge transfer material and disazo pigments as shown in the following Table 6 were used.

The electrophotographic elements Nos. 1 to 20 thus prepared were subjected to -6 KV corona discharge for 20 seconds by an electrostatic copying paper tester (SP428 Type produced by Kawaguchi Denki Works), and were charged negatively. Thereafter, these elements were left to stand in the dark for 20 seconds to measure the surface potential Vpo (V) at that time, and were exposed to radiation of a tungsten lamp so that the intensity of surface illumination may become 4.5 Lux. Then, the time (sec.) required until the surface potential was reduced to 1/2 of Vpo was measured, and the exposure amount E1/2 (Lux-sec) was calculated. The results thus obtained are shown in Tables 4 to 6.

                  TABLE 4                                                          ______________________________________                                         Photosensitive                                                                           Disazo        Vpo     El/2                                           Material No.                                                                             Compound No.  (volt)  (Lux · sec)                           ______________________________________                                         1         18            -1198   8.0                                            2         19            -562    6.5                                            3          3            -498    2.3                                            4         121           -1114   4.4                                            5         15            -1053   4.9                                            6         10            -798    3.2                                            7          6            -951    4.0                                            8         40            -1013   2.0                                            ______________________________________                                    

                  TABLE 5                                                          ______________________________________                                         Photosensitive                                                                           Disazo        Vpo     El/2                                           Material No.                                                                             Compound No.  (volt)  (Lux · sec)                           ______________________________________                                          9        25            -1054   10.0                                           10        29            -595    8.0                                            11        32            -833    6.0                                            12        37            -950    7.1                                            ______________________________________                                    

                  TABLE 6                                                          ______________________________________                                         Photosensitive                                                                           Disazo        Vpo     El/2                                           Material No.                                                                             Compound No.  (volt)  (Lux · sec)                           ______________________________________                                         13         3            -835    5.1                                            14         4            -942    6.4                                            15        18            -1126   6.8                                            16        15            -1111   4.3                                            17        10            -898    3.4                                            18         6            -1010   3.9                                            19        40            -1105   3.8                                            20        39            -1003   4.0                                            ______________________________________                                    

EXAMPLE 21

The same procedure as in Example 1 was repeated, except that disazo pihment No. 3 was used as a charge generating material and that a solution prepared by mixing 2 parts by weight of 4-diphenyl aminostilbene as a charge transfer material, 2 parts by weight of polycarbonate resin ("Panlight K-1300" manufactured by Teijin Kasei Co., Ltd.) and 16 parts by weight of tetrahydrofuran was coated on the charge generating layer by a doctor blade. The coated product was dried at 80° C. for 2 minutes and then 100° C. for 5 minutes, thus forming a charge transfer layer having a thickness of about 20 μm.

The results are shown as follows:

Vdo=-1092 volt

Vpo=-772 volt

Vpo/Vdo=0.71

E1/2=5.7 lux-sec

E1/5=10.4 lux-sec

E1/10=13.4 lux-sec

As can be seen from the above data, the photosensitive material of the present invention has a higher sensitivity.

The photosensitive materials Nos. 16 and 19 of the present invention were set in an electrophotographic copying machine (Ricopy-P-500 Type produced by RICOH K.K.), and the image-formation was repeated 10,000 times. As these results, each photosensitive material was found to form a clear-cut image regardless of the numerous repetition of image-formation. It should be understood from these results that the photosensitive materials of the present invention are excellent also in durability. 

What is claimed is:
 1. A photosensitive material for use in electrophotography, characterized by providing a photosensitive layer containing a disazo pigment having the following general formula (VII), ##STR170## wherein A₁ represents a coupler residue.
 2. The photosensitive material as claimed in claim 1, wherein said coupler residue A₁ has the general formula (VIII), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) or (XVI), ##STR171## (wherein X₁, Y₁, Z, m and n in the above formula (VIII), (IX), (X) and (XI) represent the following groups: X₁ : --OH, ##STR172## or --NHSO₂ --R₃ (wherein R₁ and R₂ represent hydrogen or a substituted or non-substituted alkyl group, and R₃ represents a substituted or non-substituted alkyl or a substituted or non-substituted aryl group); Y₁ : hydrogen, halogen, substituted or non-substituted alkyl group, substituted or non-substituted alkoxy group, carboxyl group, sulfo group, substituted or non-substituted sulfamoyl group or ##STR173## (wherein R₄ represents hydrogen, alkyl group or its substituted compound, phenyl group or its substituted compound, and Y₂ represents cyclic hydrocarbon or its substituted compound, heterocycle or its substituted compound, or ##STR174## wherein R₅ represents a cyclic hydrocarbon or its substituted compound, heterocycle or its substituted compound, or styryl group or its substituted compound, and R₆ represents hydrogen, alkyl group, phenyl group or their substituted compound, or R₅ and R₆ may form a ring with carbons bonded thereto);Z: cyclic hydrocarbon or its substituted compound, or heterocycle or its substituted compound; n: an integer of 1 or 2; m: an integer of 1 or 2), ##STR175## (wherein R₇ in the above formula (XII) and (XIII) represents a substituted or non-substituted hydrocarbonyl group, and X₁ is the same as mentioned above), ##STR176## (wherein R₈ represents an alkyl group, carbamoyl group, carboxyl group or its ester, and Ar₁ represents a cyclic hydrocarbon or its substituted compound, and X₁ is the same as mentioned above), ##STR177## (wherein R₉ in the above formula (XV) and (XVI) represents hydrogen or substituted or non-substituted hydrocarbonyl group, and Ar₂ represents cyclic hydrocarbon or its substituted compound).
 3. The photosensitive material as claimed in claim 1, wherein said coupler residue A₁ has the above general formula (IX), (XII), (XIII), (XIV), (XV) or (XVI), and X is hydroxyl group.
 4. The photosensitive material as claimed in claim 1, wherein said coupler residue A₁ has the general formula (XVII), ##STR178## wherein Y₁ and Z are the same as mentioned above.
 5. The photosensitive material as claimed in claim 1, wherein said coupler residue A₁ has the general formula (XVIII), ##STR179## wherein Z, Y₂ and R₂ are the same as mentioned above.
 6. The photosensitive material as claimed in claim 1, wherein said coupler residue A₁ has the general formula (XIX) or (XX), ##STR180## wherein Z, R₂, R₅ and R₆ are the same as mentioned above, and R₁₀ represents a substituent as defined in Y₂. 